ENAW Al-Mg-Si（B）鋁合金。擠壓棒材、管材
|
|
|
|
|
|
|
|
|
編號(hào)：ENAW-6101B
|
|
|
|
|
|
|
|
|
分類：鋁-6000系列（鎂和硅是主要合金元素）
|
|
|
|
|
|
|
|
|
標(biāo)準(zhǔn)：EN 573-3:2009鋁和鋁合金。鍛造產(chǎn)品的化學(xué)成分和形式。產(chǎn)品的化學(xué)成分和形式
|
|
|
|
|
|
|
|
|
EN 755-2:2008鋁和鋁合金。擠壓棒材、管材和型材。機(jī)械性能
|
|
|
|
|
|
|
|
|
EN 14121:2009鋁和鋁合金。電工用薄板、帶材和板材
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical comb % of grade ENAW-AlMgSi(B) ( ENAW-6101B )
|
|
|
|
|
|
|
|
|
Fe
|
Si
|
Mn
|
Cu
|
Mg
|
Zn
|
Others
|
-
|
|
0.1 - 0.3
|
0.3 - 0.6
|
max 0.05
|
max 0.05
|
0.35 - 0.6
|
max 0.1
|
each 0.03; total 0.1
|
Al - remainder
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of grade ENAW-AlMgSi(B) ( ENAW-6101B )
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (T6)
|
215
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (T7)
|
170
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (T6)
|
160
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (T7)
|
120
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (T6)
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (T7)
|
12
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (T6)
|
6
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (T7)
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (T6)
|
70
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (T7)
|
55 - 60
|
|
|
|
|
|
|